Figure 1.5 Mold thermal controlling device (56).

      The mold thermal controlling device further includes a first surface having a first trench, and the opening of the first trench is positioned at the first surface. The cross-sectional area of the first trench tapers from the opening of the first trench along the first direction, and the mold is placed in or removed from the first trench along the first direction.

The mold thermal controlling device applies a pressure to the mold along the first direction. The surfaces of the mold that is in contact with the first temperature control layer protrudes and concaves along the first direction, and the cross section of the opening of the first trench tapers along the first direction. The mold is placed in or removed from the first trench along the first direction.

      Since the mold thermal controlling device includes a temperature control tunnel that is formed with the temperature control layer, the temperature control tunnel can efficiently heat or cool the mold placed therein. Moreover, the mold used with the mold thermal controlling device can be easily replaced, and there are structures that may be included in or on the mold to assist the positioning of the mold, the gas discharge or to perform a grabbing action. Additionally, the mold thermal controlling device may be applied to an automated fabrication process. Since the hot press system of the disclosure includes the above mold thermal controlling device, which can provide heating or cooling with high efficiency, the hot press system of the disclosure can be broadly applied to various hot pressing processes (56).

1.14 Stamper Mold

       1.14.1 Recoding Media

      A stamper for forming a data recording region on a recording medium substrate by means of a transfer surface thereof has been described (57). The transfer surface transfers a predetermined set of data to the recording medium substrate. The stamper is fitted on at least one of the metal molds that are arranged opposite one another for forming the recording medium substrate. The stamper includes a stepped portion formed as bends in the material of the stamper. The stepped portion is configured to project from the transfer surface toward the recording medium substrate.

      The substrate may be produced through common injection molding processes and photopolymer processes. The injection molding process is a process in which an acrylic or a PC resin melted by a plasticizer of a molding device is filled into a cavity of a mold fitted with a master disc having microscopic projection/recess patterns for recording/retrieving signals, and the resulting substrate is removed from the mold after the molten resin cools down and is solidified (57).

       1.14.2 Microscopic Structured Body

      A polymer molded product with a fine structure has been increasingly utilized in various fields such as electronic devices, optical devices, recording media, and medical devices (58). Various methods for manufacturing such a molded product with fine structure have been proposed but attention has been attracted to a UV and thermal nanoimprint method owing to high economic efficiency and productivity. In the case of nanoimprint methods, there is a hot embossing, i.e., a thermal nanoimprint method, in which a stamper mold is pressed to a polymer substrate softened under heating to cause plastic deformation, thereby transfer-molding a pattern of the stamper mold. The hot embossing method shows a high productivity and has advantages such as the capability of fabrication of fine patterns of various thermoplastic polymer substrates.

      However, the thermal nanoimprint method has a problem as, in the filling stage of a fine structure of a high aspect ratio, the fluidity of the polymer is insufficient or a high pressure is needed. Also, the hot embossing method has a problem that, when the polymer is heated to the melting temperature, the fluidity of the polymer exceedingly increases and the polymer substrate only undergoes deformation of extending in a plane direction even when pressed, and thus the polymer is not filled into a deep groove portion of the fine structure in which flow resistance is large.

      To address this problem, a method of manufacturing a molded product with a nanostructure and a microstructure has been proposed, which includes (59, 60):

      On the other hand, besides the hot embossing method, there is a UV optical nanoimprint method in which, after a liquid photocurable polymer is coated on a substrate at room temperature, an optically transparent stamper mold is pressed to the polymer and the polymer is irradiated with a light through the stamper mold to cure the polymer, thereby transcribing a pattern onto the polymer substrate. The advantages of the UV optical nanoimprint method are that processing can be performed at room temperature, transcribed pressure is low, and a highly accurate pattern can be molded (58).

      However, in the UV optical nanoimprint method, although the pressure for transcription is low, a photocurable polymer generally exhibits a small amount of shrinkage at curing and has properties resembling an adhesive, so that it is difficult to release the imprinted film polymer from the stamper mold and thus there is a concern that a fine structure of the stamper mold will be broken through releasing the imprinted film (58).

      To adddress this problem, a manufacture method has been proposed in which a replica is formed based on the stamper mold original plate (61). The replica is used as a stamper mold in the UV optical nanoimprint step.

      This method for manufacturing a polymer-made imprinted film with a fine structure having a minimum processing size of 1,000 nm or less includes (61):

The above-described methods (59–61) for manufacturing a molded product with fine pattern are methods of performing a transfer-molding by pressing a heated polymer substrate or a molten polymer to a stamper mold having a fine structure. Such methods require the pressurization of a stamper mold having a nanoscale fine structure. A high degree of concern exists of breaking the stamper mold.

      On the other hand, in electronic devices, optical devices, recording media, and biodevices, an attempt has been made to further improve their functionality by a molded product with a fine nanostructure, so there is a demand for a manufacturing method capable of manufacturing a molded product with fine nanostructure stably using various materials (58).

      A method for manufacturing a molded product with a fine structure consists of the following steps (58):