et al. 2017). Inorganic pigments are based on metals and can be divided into three classes: white pigments (TiO2), carbon black (CB), and special effect pigment (Huckle and Lalor 1955). TiO2 is the most widely used pigment in the plastic industry due to its high refractive index and ability to provide a high degree of opacity and whiteness. In addition, TiO2 is known for its excellent durability and general nontoxicity. Black pigmentation in plastics is typically based on CB, the second most used pigments in volume by the plastic industry. CB also has dual functionality in that it can also act as a reinforcing filler, conductive filler, and light stabilizer improving the weatherability and stability of the plastic (Huang 2002). Special pigments impart vibrant colors to plastic materials and include fluorescent pigments, pearlescent pigments (mica coated with TiO2), and metallic pigments (aluminum bronzes, copper, copper‐zinc alloys, and zinc).

      2.2.9 Fillers and Reinforcements

      Fillers are relatively cheap, solid substances that are added to plastic formulations in high percentages to adjust volume, weight, and mechanical performance (Zweifel et al. 2001). Inert fillers often do not compromise the functional properties of the plastic; they are cheaper than resin and can significantly reduce the cost of the formulation. Fillers can also serve as reinforcing agents that improve the mechanical performance and durability of the plastic. They are used as powders, fibers, or nanotubes.

      Filler consumption globally in 1999 was 66% calcium carbonate, 6% talc, 6% clays, 3% wollastonite (CaSiO3), and the remaining 19% included silica, glass, asbestos, alumina, rutile, CB, and carbon nanotubes (CNTs; Civancik‐Uslu et al. 2018; Zweifel et al. 2001). Reinforcements are generally strong fibers including glass, carbon, or aramide fibers (Alam et al. 2019; Hansen et al. 2013). Fillers and reinforcements are used virtually in all polymers, but the largest fraction (i.e. over 90%) is used primarily in rubbers, PVC, and polyolefins. The improved mechanical properties in a filled plastic are derived from the interface layer between the polymer and the filler. The stronger the interfacial interactions, the better the mechanical performance of the composite (i.e. polymer/filler mix). The efficacy of the filler is also dependent on adequate dispersion in the polymer matrix. Good dispersion is achieved through extrusion, dispersing agents, or by surface treatment of the filler to improve compatibility with the polymer matrix.

      Fillers can be microscopic (1 μm) or macroscopic (<100 μm) in size and have a very low propensity to leach out of the plastic. However, degradation and wear of a filled plastic can release fibers into surrounding environments either during use or after disposal (Froggett et al. 2014). In addition, the use of nano‐particulate fillers, such as CNTs or silica nanoparticles (silica‐NPs), has gained popularity over the past 20 years due to the superior material properties of nanocomposites when compared to conventional composites. Currently, commercial availability is low as these materials are relatively new. Nonetheless, production volumes are increasing with market sizes projected to grow significantly (Hendren et al. 2011).

      Many discussions on movement of plastic additives within the ocean focus on the plastic itself as the main carrier but it is not the only significant transport mechanism (Zarfl and Matthies 2010). Koelmans et al. (2016) states that the fraction of hydrophobic organic compounds (HOCs), including organic additives, held by plastic is negligible compared to that held by other media (i.e. seawater, atmosphere, sediment, and biota), implying the plastic‐mediated transport to be generally unimportant in terms of HOC abundance.

Schematic illustration of complex sources and transport of plastic additives to, from, and within the ocean.

      Source: United States Environmental Protection Agency (2021). Toxic Release Inventory National Analysis 2019.

Скачать книгу


Chemical name Abbreviation Additive class Total onsite and offsite disposal (metric tons)
Styrene Monomer 14,742
Nonylphenol NP Antioxidant/surfactant 142
Dimethyl phthalate DMP Plasticizer 69
Dibutyl phthalate DBP Plasticizer 135
PBBs PBB Flame retardant 0.6
Hexabromocyclododecane HBCD Flame retardant 60
Tetrabromobisphenol A