LITMIR.BIZ

Figure 1.2 Depiction of MOF-5 (Zn₄O(BDC)₃) as one of the most well-known MOFs. MOF-5 is synthesized using zinc nitrate and 1,4-benzenedicarboxyxlic acid (H₂-BDC). In self-assembly process Zn(II) ions and deprotonated 1,4-benzenedicarboxyxlic acid bond together through coordination interactions between Zn(II) ions and BDC²⁻linkers to develop MOF-5 in solid phase [5].

In 2013, IUAC recommended that CP could be defined as a “coordination compound with repeating coordination entities extending in 1, 2, or 3 dimensions” while MOF is defined as “coordination network with organic ligands containing potential voids” [6]. It is necessary to mention that IUPAC defines coordination networks as a “coordination compound extending through repeating coordination entities in 2 or 3 dimensions” [6]. Based on these recommendations it could be concluded that CPs could be 1D, 2D or 3D with repetitive building blocks connected with coordination interactions while MOF are porous with hybrid organic–inorganic nature and they are at least extended in 2 dimensions. Also, there is another hidden point in these IUPAC definitions which must be clarified. In these definitions there is no persistence on crystallinity of the materials. In other word, it is not mentioned that CPs must be crystalline. It means that crystalline porous materials based on coordination interactions are coordination polymers while CPs could be both crystalline and amorphous. In another common approach about MOFs and CPs, it is realized that porous 3D structures may be called as MOFs [7]. In conclusion, the most important differences between MOFs and CPs revolve around their dimensionality and porosity [8].

1.2 Metal–Organic Frameworks

      After pioneering works of Yaghi in 1995 [9], a remarkable number of chemists and material engineers are engrossed in design and application of MOFs. Such great interest among scientists is because of their unique characters which make MOFs suitable for diverse industrial and real-life applications [10, 11].

      As mentioned, MOFs are constructed based on organic and inorganic building blocks. In most cases, organic ligands are ditopic or polytopic O-donor ligands based on carboxylates linkers or N-donor ligands based on pyridine pillar spacers. Metal-containing units founded on different kind of metal ions, mostly based on lanthanide cations (like Ln(III), Tb(III), Eu(III), Dy(III) and Sm(III)), transition metals (like 3d cations like Zn(II), Cu(II), Ni(II), Co(II), Fe(III) or Fe(II), Mn(II) and Cr(III) or Cr(II) and heavy transition metals like Cd(II), Zr(IV), Hf(IV)) and main metal ions (Al(III), or some of alkaline or alkaline-earth cations). As a result of such diversity in selection of building blocks, unlimited number of MOFs with different structural and practical properties can be developed by changing metal ion/clusters, using various combinations of these inorganic building blocks and infinite types of organic linkers with different lengths, functionalities and geometries. Additionally, since MOFs are developed based on organic and inorganic building blocks, their hybrid organic–inorganic nature is suitable for tuning the structure and application of MOFs.

MOFs are synthesized by coordination of organic linker to inorganic units by strong bonds [12]. These connections between organic and inorganic building blocks through coordination interactions are such that they create vacant spaces (pores) between the each individual building block. As a result of such porosity, MOFs provide accessible pore volume in the bulk of the materials moreover than accessible area at the surface of material. Right selection of the building blocks makes it possible to vary some parameters, such as the pore size (to increase pore diameter to 98 Å), density (to decrease to 0.126 g·cm⁻³) and surface area (typically in range from 1,000 to 10,000 m²·g⁻¹) which are exceeding those of traditional porous materials such as zeolites and carbons [13]. In summary, porosity and surface area of MOFs could be tuned through right selection of organic ligands with correct size, flexibility and appropriate inorganic nodes.

      The nature, strength and the number of coordination interactions between organic and inorganic building blocks of MOFs are the main reasons for evaluation of their stability. On one hand, selection of building blocks based on Hard-Soft acid-based theory is very beneficial for synthesis of highly stable MOFs [14]. For example hard metal ions such as Al(III) and Zr(IV) [15] could develop stable MOFs through connection with carboxylate-donor organic linker because these building blocks are hard Lewis acid and base, respectively. Another group of stable MOFs are based on selection of soft metal ions like late 3D metal ions and soft N-donor organic ligands like pyrazolate based linkers. On the other hand, the number of coordination bonds between inorganic nodes and organic linkers is another critical factor on the stability of MOFs. The higher number of coordination bonds, the higher stability of the MOF.

      Another desirable character of MOFs is their crystalline structure. Selection of well-defined individual molecular building blocks could develop regular structure and periodic frameworks. As a result of their regular crystalline structure, we can tune their chemical and physical properties through logical designing of the framework and right selection of building blocks.

One of the most important advantages of MOFs from other conventional polymers or porous materials is the fact that we can tailor their chemical properties through rational choice of functional groups. Tunability in chemical functionality of MOFs could be provided via three functionalization strategies including selection of functional organic ligand, functionalization

Скачать книгу